High-temp Battery Cartridge,Double Insulation Sleeve,High-strength Insulation Ring,C CE fiber ring Motor Shaft

High-temp Battery Cartridge,Double Insulation Sleeve,High-strength Insulation Ring,C CE fiber ring Motor Shaft  china WELLELE.com ,EM salefiber@yahoo.COM make

Epoxy glass fiber entwined sleeve,High-temp Battery Cartridge,Double Insulation Sleeve,High-strength Insulation Ring,C CE fiber ring wall thickness: >0.5mm; size precision: High; inner bore tolerance: <0.05mm; external diameter tolerance: <0.10mm; high concentricity and good straightness;-temperature resistance: Grade F/H/C; appearance: Semitransparent and light green for conventional products or other customized colors, featuring smooth surface; high mechanical strength, and excellent corrosion resistance.-General length: 365mm, 785mm, 970mm, 1,118mm, 1,455mm, etc.Major Advantages:-Assembly equipment-Simple compressing and simple support tools-Precision and automation equipment production (600pcs/hr)-Reduce obsolescence cost-As everyone knows, moulding generates pores in material production, causing a mass of wastes and resulting in failure of hi-pot test

wellele.com ,sale@wellele.com

-Tubes can be extruded, and residual components can be reused (reprocessed).

-Design for exerting the best motor performances

-UL register materials (AFW G-10)Other Advantages

-Flexible design-good in any size-Reduce design change realization time

-The ordering delivery time of reassembly is only 4-6 weeks

Data of Fiberglass Ring

PropertiesUnitTypical*Color

*Resin content ( weight % )

*Glass fiber content ( weight % )

*Composit density

*Circumferential tensile strength

at 20°C

(NOL test )

*Temperature at which the residual of

 Initial tensile strength is greater then

85%

*Fiber diretion thermal expansion coefficient (CTE)

*Thermomechanical analysis:

Glass transition temperature

(ASTM E 1545-93 )

%

%

g/cm3

Mpa

(PSI)

°C

(°F)

1/K

°C

(°F)

Light brown

16-23

84-77

2.10-2.20

800-1200

(116000-174000)

300°C

(572°F)

8.50E-06

300-350°C

(572-662°F)

NOTE:

Mechanical NOL data vary within a range determined by resin content and the ratio diameted thickness of the ring .This ratio gives a flexural mode that will cocur during test and test data can vary for each type of ring.-Temperature index: 180°C

 UL 94 burning